Accurate in-situ lattice matching by reflection high energy electron diffraction

ABSTRACT

An in-situ method is disclosed for highly accurate lattice matching using reflection high energy electron diffraction dynamics. The method includes the steps of providing a substrate of a first semiconductor material and initiating growth of a second semiconductor material thereon. The oscillation amplitude of intensity I of waveform cycles is monitored using reflection high energy electron diffraction. A maximum intensity I +  and a minimum intensity I -  is determined over a predetermined number of waveform cycles. The intensity drop ΔI from initial reflectivity to minimum reflectivity of the waveform cycles is determined and normalized figure of merit FM is calculated for the predetermined number of waveform cycles using the relationship: ##EQU1## The fluxes of the second semiconductor material are then adjusted to maximize FM and optimize matching. A multiple quantum well light modulator is also provided including a semiconductor substrate of InP, a multiple quantum well region, disposed above the InP substrate, composed of InGaAs and having a thickness of about 4 μm. The modulator is characterized by a lattice mismatch of less than 2×10 4 .

This is a divisional of application Ser. No. 08/263,305 filed Jun. 21, 1995, now U.S. Pat. No. 5,480,813.

BACKGROUND

1. Technical Field

The present invention relates to an accurate in-situ growth technique based upon reflection high energy electron diffraction dynamics for accurate lattice matching of dissimilar materials.

2. Discussion of Related Art

The invention of low loss optical fibers for use as a practical optical transmission medium has stimulated tremendous growth in other areas relating to optical communications. The term "optical" as used herein refers not only to visible light but to any electromagnetic radiation which can be transmitted within dielectric fibers. The term refers to electromagnetic radiation generally of wavelength between 0.1 and 50 microns. Recently, fiber to the home systems have been proposed which would utilize surface normal electroabsorption modulators to convert downstream light into upstream dam. One such system uses a single fiber to connect two locations and effects bidirectional data transmission over this fiber using a single laser. See, e.g., T. Wood et al., Elec. Lett., Vol. 22, pgs. 346-352 (1986) and T. Wood et al., J. Light Tech., Vol. 6, pages 527-528 (1988) the disclosures of which are incorporated herein by reference. This system uses a light modulator that imprints data on the fiber return and thus avoids the need for a second laser at the subscriber location. Particularly useful for modulation are electrooptic devices whose optical properties, such as absorption or index of refraction, may be varied by application of an appropriate electrical signal. Exemplary of such electrooptical devices is the multiple quantum well (MQW). The MQW includes a plurality of layers of different semiconductor materials such as gallium arsenide (GaAs) and aluminum gallium arsenide (AlGaAs). Other examples of suitable materials include such III-V systems a InAs/GaAs,(In,Ga)As/GaAs,(In,Ga)As/InP and (In,Ga)As/(In,Al)As. The layers alternate between wide bandgap material and narrow bandgap material. Appropriate selection of materials, compositions and layer thicknesses permits fabrication of unique electrooptic devices.

When used as a modulator, the MQW exhibits a significant shift in the absorption edge due to the change in the confinement energy associated with the applied electric field and consequent distortion of the well. This shift in absorption is the basis for the MQW as a modulator. Since the applied field can significantly alter the light absorption properties of a properly biased MQW, light passing through the MQW will be modulated.

In the fabrication of MQW's, thin films of the semiconductor materials are grown or deposited onto substrate material in a wide variety of reactors. One such reactor is a molecular beam epitaxy (MBE) reactor. See, e.g., U.S. Pat. No. 3,751,310 to Cho. Since 1983 it has become apparent that the period of oscillatory behavior observed in the intensity of the RHEED features on initiation of growth is directly related to the growth rate. See, e.g., J. H. Neave et at., Appl. Phep. A31,1 (1983) and J. M. VanHove et al., J. Vac. Sci. and Technol. B1,741, (1983) the disclosures of which are incorporated herein by reference. In fact, monitoring of the RHEED intensity oxillations has become an established technique for the in-situ calibration of beam fluxes and the control alloy compositions for the growth of lattice matched heterostructures. The accuracy of the analysis of the RHEED oscillatory data, for a thin layer GaAs/AIGaAs material system, is about 1%. See, e.g. Turner et al., J. Vac. Sci. Technol. B8, 283 (1990). Hence, there is a real need for a technique which allows accurate lattice matching conditions to be arrived at in a quick and reproducible manner for the realization of a variety of semiconductor optical devices such as, for example, modulators, lasers and detectors.

SUMMARY

An in-situ method is disclosed for highly accurate lattice matching using reflection high energy electron diffraction dynamics. The method includes the steps of providing a substrate of a first semiconductor material and initiating growth of a second semiconductor material thereon. The intensity I of a diffraction feature generated by using an electron beam (RHEED) is monitored versus time. A normalized figure of merit FM is calculated by using the relationship: ##EQU2##

By maximizing the value of FM, accurate lattice matching on the order of about two parts in ten thousand can be obtained.

A multiple quantum well light modulator is also provided including a semiconductor substrate of InP, a multiple quantum well region, disposed above the InP substrate, composed of InGaAs quantum well and InP barriers and having a thickness of about 4 μm. The modulator is characterized by a lattice mismatch of less than 2×10⁻⁴.

BRIEF DESCRIPTION OF THE DRAWINGS

Various methods are described hereinbelow with reference to the drawings, wherein:

FIG. 1 is a schematic illustration of a reflectivity measurement test set up for characterization of electroabsorption modular devices;

FIG. 2 is a plot of RHEED intensity oscillations for different In and Ga flux ratios;

FIG. 3 is a plot of the variation in oscillation amplitude for a systematic change in lattice mismatch;

FIG. 4 is a compilation of three plots, plot B showing RHEED Intensity Oscillations for InP growth on InP, Plot A showing RHEED Intensity Oscillations for InGaAs on InP and RHEED Intensity Oscillations for InGaAs on InGaAs with FIG. 4A showing a Fast Fourier Transform of the InP on InP RHEED oscillations;

FIG. 5 is a High Resolution X-ray Diffraction scan of a p-i-n modulator incorporating 225 InGaAs/InP MQW's in the intrinsic region;

FIG. 6 is a plot of reflectivity spectra at 300K of InGaAs/InP MQW.

FIG. 7 is a plot of contrast ratio at exciton at 300K of InGaAs/InP MQW;

FIG. 8 is a plot of contrast ratio below band edge at 300K of InGaAs/InP MQW;

FIG. 9 is a plot showing RHEED intensity oscillations for different InGaAs lattice mismatches on InP.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The invention will now be described in detail in connection with the drawings. FIG. 1 is a schematic drawing of a preferred embodiment of a measurement test set up, shown generally at 20 for use with the invention as applied to a modulator. Surface normal modulators are attractive candidates for fiber to the home applications where their amenability to processing in large two dimensional arrays would help keep unit costs down. In order to be useful, however, contrast and absorption values must be acceptable in the 1.3 to 1.55 μm regime corresponding to the low dispersion, low loss windows for optical fibers.

Surface normal In₀.53 Ga₀.47 As/InP MQW modulators operating at 1.55 μm are particularly attractive for this application. Such systems need modulators with on-off ratios of between 8:1 to 10:1 at 155 μm. However, the absorption coefficient exhibited by this material system is only about 40% of the value exhibited by the GaAs/AIGaAs material system. In order to overcome this drawback an intrinsic MQW region over 4 μm thick must be employed. At this thickness, lattice mismatches of several parts in 10⁻⁴ can cause strain relief resulting in an inhomogeneously broadened exciton and thereby a reduced contrast ratio. Highly accurate lattice matching thus becomes very important.

To achieve this objective with a high yield, an in-situ growth approach based on RHEED dynamics is disclosed that allows InGaAs to be accurately lattice matched to an InP substrate. This approach is based on an analysis of the intensity amplitude as opposed to conventional approaches wherein growth rates are determined by an analysis of oscillation frequency. FIG. 1 is a schematic illustration of a reflectivity measurement test set up for characterization of electroabsorption modulator devices.

FIG. 2 shows a plot of the intensity oscillation of RHEED for different In and Ga flux ratios. Accurate lattice matching conditions are shown in FIG. 2 as clearly defined oscillations. But for slight mismatches, the RHEED oscillation amplitude is degraded both for Ga and In rich lattice mismatches. Even though the intensity oscillation amplitude has significantly changed (because of the mismatch) the oscillation frequency does not show a reproducible change. In fact, it is not possible to detect a change in oscillation frequency with reliability to better than 1%. FIG. 3 is a plot of the FM for a systematic change in lattice mismatch. Clearly the peak establishes perfect lattice matching conditions. The scale shows that mismatches as low as a few parts in 10⁴ can be easily distinguished. This method has other application to many Group III-V systems such as, for example, InGaP/GaAs, GaAsSb/InP or ternaries, quaternaries under lattice matched conditions.

EXAMPLE 1

To exemplify the viability of this approach measurements were made on p-I(MQW)-n surface normal modulators incorporating thick intrinsic regions where the new process was used to obtain highly accurate lattice matching conditions. The data also shows that even mismatches of a few parts in 10⁻⁴ result in an inhomogeneous broadening of the excitonic resonance and hence a degradation of performance. See Table 1.

The structures were grown by Gas Source MBE in a VG-80H M BE system modified to handle gas flow. Pure AsH₃ and PH₃ constituted the Group V fluxes, while elemental Ga and In were used as the Group III sources. A standard VG electron gun, operated at 15 KV with a filament current of 2.25 A is used to generate the RHEED pattern. The image generated on the phosphor screen is captured with a CCD camera which sends it to a TV monitor and also to a frame grabber card capable of 256 bit resolution located in a 486 desktop PC for display on the video monitor. The card is capable of sampling the image 30 times a second. Software written for this card allows the user to define boxes of different pixel sizes which function as a detector. By aligning the pixel box over a diffraction pattern, feature RHEED intensity oscillations can be recorded. The position of this aligned box pixel, once defined, remains fixed. Hence, once an aforesaid pixel box is defined and fixed any lateral drift in the diffraction geometries can be corrected for by realigning the diffraction spot within the confines of the pixel box A typical calibration run consists of recording the RHEED oscillations, and then transporting the data file to a program which allows us to perform both time and frequency domain analysis on the acquired data set. Using this setup a variance on the order of 1% in the growth rate between consecutive measurements can be achieved.

For our experiments RHEED intensity measurements were performed on a small (˜0.5 cm⁻²)n+InP wafer positioned at the center of a molybdenum block with indium. Use of a small RHEED sample further minimizes any error. Further, the flux distribution over such a small piece can be assumed to be uniform. After thermal desorption of the oxide under a P flux, a layer of InP was first grown for an hour so as to allow the In cell to reach thermal equilibrium. At the same time, the Ga cell was also brought up to temperature and held with the shutter closed. All measurements were made at a growth temperature of 500° C. on a Group V stabilized ×2 reconstruction along the [110] azimuth. The Group V to Group III flux ratio was maintained at approximately 2.5:1.

All the measurements were made on a fresh, fully recovered InP surface. Prior to initiating growth of InGaAs, the Group V gases were switched and AsH₃ was allowed to flow into the chamber for 30 sec. RHEED intensity data was then acquired from the specular spot of the diffraction pattern with a 5×5 pixel sized box over 75 sec. (30 sec. of actual intensity oscillations plus 45 sec. to record the recovery characteristics) at a sampling rate of 30 Hz. Upon completion of the measurement the Group V gases were once again switched and InP grown for 3 minutes before repeating the measurement. The set point of the In cell was held constant throughout the measurement sequence, while the Ga cell temperature was stepped to lower values. A five minute layer of InP was inserted between each successive change in Ga set point.

As can be see in FIG. 2, qualitatively different forms of oscillations were encountered corresponding to situations where the composition was either Ga rich, In rich or lattice mismatched by small amounts. For In rich or lattice matched even by slight amounts under these conditions it was not possible to detect a reproducible change in the oscillation frequency as seen in FIG. 2.

Correlating lattice mismatch obtained from high resolution X-ray diffraction (HRXRD) measurements and measured linewidths from 77KPL measurements on p-i(MQW)-n devices containing thick MQW intrinsic layer shows that even small amounts of lattice mismatch leads to strain relief leading to an associated inhomogeneous broadening of the excitonic resonance.

Results

FIG. 4 shows RHEED Intensity oscillations for growth very close to lattice match conditions. In Plot B, the oscillations observed for InP growth on InP are the usual type expected for binary III-V growth. Here, InP exhibits sinusoidal oscillations at the periodicity of the monolayer growth rate. Initial cycles of the intensity oscillations are rapidly damped symmetrically about maximum and minimum surface disorder as time approaches a terminal configuration of equilibrium surface roughness. Oscillations eventually vanish when rate of formation of surface step density (i.e., spontaneous nucleation from growth) becomes comparable to the rate of 2-D ledge motion (i.e., steps on terraces coalescence to the step ledge). When this happens the state of surface roughness does not change with time (terminal roughness). The recovery dynamics, when measured with no In deposition, also exhibit typical behavior as evidenced by step coalescence dynamics which is single stage. This corresponding to an island size that grows in time. Final RHEED intensity after complete recovery equals initial intensity before deposition.

The inevitable damping of the oscillations is an important factor that limits lattice matching when based on conventional RHEED frequency analysis of the growth rate. A Fast Fourier Transform of the InP on InP RHEED oscillations is shown in FIG. 4A. The growth rate is Fourier Transform Limited 0.756 ML/s (center of the distribution) with a Full Width Half Maximum of 0.17 ML/s. In essence, by sampling the growth rate for an effective time of 6.0 s leads to an uncertainty in growth rate Δω/ω which is huge and impractical as a means to achieve lattice matching conditions. Alternatively, RHEED intensity oscillation observed in FIG. 9 for InGaAs growth on InP exhibit different characteristics that present a new and viable route to rapid lattice matching conditions. The differences show up in three ways and are dramatic when considering the fact that InGaAs growth in FIG. 4 is only slightly mismatched to InP (5×10⁻⁴).

First, the initial state of InGaAs on InP growth oscillations that exhibit asymmetrical damping characteristics. They depict initial damping of growth oscillations from configurations of maximum and minimum surface disorder that clearly differ from the symmetrical case observed for InP growth. In addition, the recovery dynamics for InGaAs on InP show distinct differences from InP recovery in two ways. First, time evolution in recovery dynamics is complex with evidence of multiple components present. Secondly, terminal intensity after recovery is significantly lower than initial InP intensity. All three differences appear to associate with increased surface step disorder that is associated with mismatched growth. In essence, because of the difference in a real monolayer density of the mismatched flux with the substrate additional surface steps are created to conserve total surface area. The surface steps from mismatched growth are additive to those normally generated by spontaneous nucleation during growth. The first few cycles of asymmetrical damping show that the surface steps from the mismatch are rapidly formed within the first four monolayers deposited. Also, the multicomponent recovery characteristics and lower total surface reflectivity correspond to island coalescence to a new configuration of surface steps on InP because of the mismatched growth.

To quantify this approach as a route to accurate in-situ lattice matching a normalized figure of merit, FM, is defined for the initial oscillation quality to be the sum of (I⁺ -I⁻)/ΔI over the first four consecutive ML cycles measured. I⁺ (I⁻) correspond to maximum (minimum) intensity of each waveform cycle whereas ΔI is the intensity drop from initial InP reflectivity to minimum reflectivity of the oscillation waveform during deposition. When the FM for the various growth cases in FIG. 4 is plotted, (plots A and B), the FM drops by a factor four from InP growth on InP to InGaAs growth in InP. The FM for InGaAs on InGaAs is 20% larger than InGaAs on InP because mismatched surface steps remain from the first sequence of InGaAs deposition on InP. For the latter case the asymmetry in oscillation damping has improved whereas InP intensity is 25% larger than recovered intensity after first InGaAs deposition. Recovered intensity after second InGaAs deposition equals recovered intensity after first InGaAs deposition.

FIG. 9 shows RHEED oscillations observed for different InGaAs mismatches on InP. This sequence was obtained by holding the In deposition rate fixed while varying the Ga growth rate from Ga rich to In rich conditions. Clearly, RHEED intensity during InGaAs deposition show systematic difference in the oscillation quality, recovery characteristics and intensity response. From the plot, a Ga cell temperature of 910.0° C. is very close to lattice matched conditions.

In FIG. 3, the FM is shown over the same range of mismatch at finer step size than the coarse display of FIG. 9. The FM is highly sensitive to mismatch and is strongly peaked at a lattice matching condition. The degradation in FM versus mismatch is symmetrical about Ga and In rich conditions with shape reminiscent of quality characteristics obtained by PL or X-ray diffraction measurements. Upon thick InGaAs layer deposition atop these sequences lattice matching on the basis of X-ray diffraction should be at the arrowed position.

A typical HRXD scan of a p-i-n modulator incorporating 225 InGaAs/InP MQW's in the intrinsic region is shown in FIG. 5. The average lattice mismatch is obtained by determining the angular separation between the zeroth order peak (which corresponds to the reflection from the layer with the average lattice parameter of the super lattice stack) and the reflection from the substrate peak. In Table-1 the values of linewidth as determined from 77K photoluminescence measurements are presented along with the mismatch values as determined from the HRXD measurement. As can be seen even small increases in the lattice mismatch result in a significant broadening (by a factor of almost two in going from a few parts in 10⁻⁵ to a few parts in 10⁻⁴) in the linewidth of the photo luminescence (PL) spectra. In device terms this broadening of the excitonic resonance means that to red shift the exciton from under the zero field E1-HH1 peak a higher electrical field is required, which further broadens the exciton due to associated polarization of the electron-hole pair, and hence the performance is degraded.

                  TABLE 1                                                          ______________________________________                                         PL FWHM(meV)      Lattice mismatch, .increment.a/a                             ______________________________________                                         6.75              3.929 × 10.sup.-5                                      9.217             1.9647 × 10.sup.-4                                     11.472            2.59 × 10.sup.-4                                       ______________________________________                                    

Referring to FIG. 6, the reflectivity spectrum over an applied reverse bias range of 0 to 50V is plotted. The half width half maximum (HWHM) of the zero applied bias exciton peak is 6.2 meV and the whole spectrum shows a good quantum confined stark effect (QCSE), with the peak shifting by more than 50 nm without significant broadening over the entire applied voltage range.

Referring now to FIGS. 7 and 8, the contrast ratios for the normally off and normally on states calculated from the reflection spectra are shown. A high contrast ratio of better than 8:1 is achieved by operating the exciton resonance at an applied reverse bias of 50V. Moreover, the bandwidth for greater than 3:1 contrast ratio, obtained at lower drive voltages is over 20 nm for both λ₀ and λ₁ modes of operation.

Thus, accurate in-situ lattice matching using RHEED dynamics has been presented. Use of this method has been applied to the growth of high contrast surface normal Multiple Quantum Well light modulators operating at 1.5 μm. What has been described is merely illustrative of the application of the principles of the present invention. Other arrangements and methods can be implemented by those skilled in the art without departing from the spirit and scope of the present invention. 

We claim:
 1. A multiple quantum well light modulator comprising:a semiconductor substrate formed of InP, transparent to incident light; a multiple quantum well region, disposed on said InP substrate, composed of alternating films of InGaAs and InP, said substrate and said multiple quantum well region having a thickness of at least 4 μm and having a lattice mismatch of less than 2×10⁻⁴ ; said multiple quantum well light modulator exhibiting a contrast ratio of at least 8:1 when operated in a reflectivity mode with a single incident light beam having a wavelength in the range of about 1.5 to 1.6 μm.
 2. The multiple quantum well modulator according to claim 1, exhibiting said contrast ratio when operated with a reverse bias voltage of at least 40V.
 3. A multiple quantum well modulator fabricated by the steps of:(a) providing a substrate of a first semiconductor material; (b) initiating growth of a film composed of a second semiconductor material on the substrate; (c) monitoring intensity I of reflection high energy electron diffraction spot of the film and the substrate over multiple waveform cycles; (d) determining a maximum intensity I⁺ and a minimum intensity I⁻ of each waveform cycle; (e) determining an intensity drop ΔI from initial reflectivity, measured prior to initiating growth, to minimum reflectivity measured after starting growth; (f) calculating a normalized figure of merit FM for each said waveform cycle wherein

    FM=(Σ(I+-I-) )/ΔI

for each said waveform cycle; (g) adjusting cell temperature to maximize FM and optimize lattice matching: and (h) repeating steps (c)-(g) to form a plurality of alternating films of said first and second semiconductor materials, said alternating films forming a multiple quantum well region of at least 4 μm thick and having a lattice mismatch of less than two parts in 10⁴, and said multiple quantum well modulator exhibiting a contrast ratio of at least 8:1 when operated in a reflectivity mode with a single light beam of a wavelength in the range of about 1.5 to 1.6 μm.
 4. The multiple quantum well modulator according to claim 3, wherein said first semiconductor material comprises InP, said second semiconductor material comprises InGaAs, and wherein said multiple quantum well modulator exhibits said contrast ratio of at least 8:1 when operated with a reverse bias voltage of greater than 40V. 